Films of α-Ga 2 O 3 grown by Halide Vapor Phase Epitaxy (HVPE) were irradiated with protons at energies of 330, 400, and 460 keV with fluences 6 × 10 15  cm −2 and with 7 MeV C 4+ ions with a fluence of 1.3 × 10 13  cm −2 and characterized by a suite of measurements, including Photoinduced Transient Current Spectroscopy (PICTS), Thermally Stimulated Current (TSC), Microcathodoluminescence (MCL), Capacitance–frequency (C–f), photocapacitance and Admittance Spectroscopy (AS), as well as by Positron Annihilation Spectroscopy (PAS). Proton irradiation creates a conducting layer near the peak of the ion distribution and vacancy defects distribution and introduces deep traps at E c -0.25, 0.8, and 1.4 eV associated with Ga interstitials, gallium–oxygen divacancies V Ga –V O , and oxygen vacancies V O . Similar defects were observed in C implanted samples. The PAS results can also be interpreted by assuming that the observed changes are due to the introduction of V Ga and V Ga –V O . 

We report on growth and electrical properties of α-Ga₂O₃films prepared by halide vapor phase epitaxy (HVPE) at 500 °C on α-Cr₂O₃buffers predeposited on sapphire by magnetron sputtering. The α-Cr₂O₃buffers showed a wide microcathodoluminescence (MCL) peak near 350 nm corresponding to the α-Cr₂O₃bandgap and a sharp MCL line near 700 nm due to the Cr⁺intracenter transition. Ohmic contacts to Cr₂O₃were made with both Ti/Au or Ni, producing linear current–voltage ( I– V) characteristics over a wide temperature range with an activation energy of conductivity of ∼75 meV. The sign of thermoelectric power indicated p-type conductivity of the buffers. Sn-doped, 2- μm-thick α-Ga₂O₃films prepared on this buffer by HVPE showed donor ionization energies of 0.2–0.25 eV, while undoped films were resistive with the Fermi level pinned at E_Cof 0.3 eV. The I– V and capacitance–voltage ( C– V) characteristics of Ni Schottky diodes on Sn-doped samples using a Cr₂O₃buffer indicated the presence of two face-to-face junctions, one between n-Ga₂O₃and p-Cr₂O₃, the other due to the Ni Schottky diode with n-Ga₂O₃. The spectral dependence of the photocurrent measured on the structure showed the presence of three major deep traps with optical ionization thresholds near 1.3, 2, and 2.8 eV. Photoinduced current transient spectroscopy spectra of the structures were dominated by deep traps with an ionization energy of 0.95 eV. These experiments suggest another pathway to obtain p–n heterojunctions in the α-Ga₂O₃system.